单调及循环加载下大理岩断裂特性研究

doi:10.13722/j.cnki.jrme.2019.0022

Abstract
Figure/Table
References (0)
Related Citation (15)

Download: PDF (738 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract Based on the laboratory basic mechanical tests of marble，the PFC3D was used to obtain a set of mesoscopic parameters reflecting the characteristics of marble. Monotone and cyclic loading of cracked chevron notched Brazilian disc(CCNBD) model were carried out respectively to study the stress distribution，fracture toughness and crack propagation law of marble under different loadings. The results show that the mode-I(tensile) fracture toughness( ) of marble under two types of cyclic loading have different amplitude reduction of the static ，and the specimens have clear tensile softening zone after the post-peak region，and subcritical crack propagation occurs. Under cyclic loading，the crack growth of the sample can be divided into three stages：initial stage，stable stage and accelerated stage. At the initial stage of loading，the number of microcracks increased significantly，and the crack growth rate was stable. At the stable stage of loading，the crack growth rate gradually decreased，and finally，the crack growth rate gradually increased，and the number of cracks increased rapidly until failure. The tensile chain distribution was more concentrated at both ends of the ligament and on both sides of the disc than the monotonic loading.

Key words： rock mechanics fracture toughness cyclic loading subcritical crack particle flow tension chain

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Yan
	LI Jiangteng

Cite this article:

ZHANG Yan,LI Jiangteng. Study on fracture characteristics of marble under monotone and cyclic loading[J]. , 2019, 38(S2): 3313-3320.

URL:

https://rockmech.whrsm.ac.cn/EN/10.13722/j.cnki.jrme.2019.0022 OR https://rockmech.whrsm.ac.cn/EN/Y2019/V38/IS2/3313

[1]	张盛. 用5种圆盘试件的劈裂试验确定岩石断裂韧度[J]. 岩土力学，2009，30(1)：12–18.(ZHANG Sheng. Determination of rock fracture toughness by split test using five types of disc specimens[J]. Rock and Soil Mechanics，2009，30(1)：12–18.(in Chinese))
[2]	戴峰，魏明东，徐奴文，等. 岩石断裂韧度CCNSCB方法渐进破坏机制与无量纲应力强度因子宽范围标定[J]. 岩土力学，2016，37(11)：3 215–3 223.(DAI Feng，WEI Mingdong，XU Nuwen，et al. Progressive fracture mechanism of CCNSCB rock fracture toughness specimens and calibration of wide-range dimensionless stress intensity factors[J]. Rock and Soil Mechanics，2016，37(11)：3 215–3 223.(in Chinese))
[3]	包含，伍法权，郗鹏程. 岩石Ⅰ型断裂韧度估算及其影响因素分析[J]. 煤炭学报，2017，42(3)：604–612. (BAO Han，WU Faquan，XI Pengcheng. Estimation of mode I fracture toughness of rock and its impact factors analysis[J]. Journal of China Coal Society，2017，42(3)：604–612. (in Chinese))
[4]	崔振东，刘大安，安光明，等. V形切槽巴西圆盘法测定岩石断裂韧度的实验研究[J]. 岩土力学，2010，31(9)：2 743–2 748. (CUI Zhendong，LIU Daan，AN Guangming，et al. Experimental study on determination of fracture toughness of rock by Brazil disk method with v-shaped grooves[J]. Rock and Soil Mechanics，2010，31(9)：2 743–2 748.(in Chinese))
[5]	吴礼舟，王启智，贾学明. 用人字形切槽巴西圆盘(CCNBD)确定岩石断裂韧度及其尺度律[J]. 岩石力学与工程学报，2004，23(3)：383–390.(WU Lizhou，WANG Qizhi，JIA Xueming. Determination of fracture toughness and scaling law of rock by cracked chevron notched Brazilian disc(CCNBD)[J]. Chinese Journal of Rock Mechanics and Engineering，2004，23(3)：383–390.(in Chinese))
[6]	吴礼舟，贾学明，王启智. CCNBD断裂韧度试样的SIF新公式和在尺度律分析中的应用[J]. 岩土力学，2004，25(2)：233–237.(WU Lizhou，JIA Xueming，WANG Qizhi. New SIF formula of CCNBD fracture toughness specimen and its application in scale law analysis[J]. Rock and Soil Mechanics，2004，25(2)：233–237.(in Chinese))
[7]	刘新荣，傅晏，郑颖人，等. 颗粒流细观强度参数与岩石断裂韧度之间的关系[J]. 岩石力学与工程学报，2011，30(10)：2 084– 2 089.(LIU Xirong，FU Yan，ZHENG Yingren，et al. Relationship between meso-strength parameters of particle flow and fracture toughness of rock[J]. Chinese Journal of Rock Mechanics and Engineering，2011，30(10)：2 084–2 089.(in Chinese))
[8]	BAGHBANAN A，TORKAN M，NOROUZI S，et al. Evaluating modes I，II and mixed mode I–II fracture toughness of crystalline rocks using discrete element method[J]. Particulate Science and Technology，2017，13(5)：26–35.
[9]	苏承东，张盛，唐旭. 砂岩巴西劈裂疲劳破坏过程中变形与强度特征的试验研究[J]. 岩石力学与工程学报，2013，32(1)：41–48.(SU Chengdong，ZHANG Sheng，TANG Xu. Experimental study on deformation and strength characteristics of sandstone Brazil during splitting fatigue failure[J]. Chinese Journal of Rock Mechanics and Engineering，2013，32(1)：41–48.(in Chinese))
[10]	杨春和，马洪岭，刘建锋. 循环加、卸载下盐岩变形特性试验研究[J]. 岩土力学，2009，30(12)：3 562–3 568.(YANG Chunhe，MA Hongling，LIU Jianfeng. Experimental study on deformation characteristics of salt rocks under cyclic loading and unloading[J]. Rock and soil Mechanics，2009，30(12)：3 562–3 568.(in Chinese))
[11]	周辉，杨艳霜，肖海斌，等. 硬脆性大理岩单轴抗拉强度特性的加载速率效应研究——试验特征与机制[J]. 岩石力学与工程学报，2013，32(9)：1 868–1 875.(ZHOU Hui，YANG Yanshuang，XIAO Haibin，et al. Study on loading rate effect of uniaxial tensile strength characteristics of hard and brittle marble-experimental characteristics and mechanism[J]. Chinese Journal of Rock Mechanics and Engineering，2013，32(9)：1 868–1 875.(in Chinese))
[12]	ERARSLAN N，WILLIAMS D J. The damage mechanism of rock fatigue and its relationship to the fracture toughness of rocks[J]. International Journal of Rock Mechanics and Mining Sciences，2012，56：15–26.
[13]	ERARSLAN N，WILLIAMS D J. Mechanism of rock fatigue damage in terms of fracturing modes[J]. International Journal of Fatigue，2012，43：76–89.
[14]	GHAMGOSAR M，ERARSLAN N. Experimental and numerical studies on development of fracture process zone(FPZ) in rocks under cyclic and static loadings[J]. Rock Mechanics and Rock Engineering，2016，49(3)：893–908.
[15]	GHAMGOSAR M，ERARSLAN N，WILLIAMS D J. Experimental investigation of fracture process zone in rocks damaged under cyclic loadings[J]. Experimental Mechanics，2017，57(1)：97–113.
[16]	ERARSLAN N . A study on the evaluation of the fracture process zone in CCNBD rock samples[J]. Experimental Mechanics，2013，53(8)：1 475–1 489.
[17]	许学良. 脆性岩石抗拉特性及其破裂机制的试验与细观模拟研究[博士学位论文][D]. 北京：北京科技大学，2017.(XU Xueliang. Experimental and microscopic simulation research on tensile characteristics and fracture mechanism of brittle rocks[Ph. D. Thesis][D]. Beijing：University of Science and Technology，2017.(in Chinese))
[18]	ISRM Testing Commission(coordinator：Fowell R J). Suggested method for determining mode I fracture toughness using cracked chevron notched Brazilian disc(CCNBD) specimens[J]. International Journal of Rock Mechanics and Mining Science and Geomechanics Abstracts，1995，32(1)：57–64.
[19]	田文岭，杨圣奇，方刚. 煤样三轴循环加卸载力学特征颗粒流模拟[J]. 煤炭学报，2016，41(3)：603–610.(TIAN Wenling，YANG Shengqi，FANG Gang. Particle flow simulation on mechanical behavior of coal specimen under triaxial cyclic loading and unloading[J]. Journal of China Coal Society，2016，41(3)：603–610.(in Chinese))
[20]	ERARSLAN N. Microstructural investigation of subcritical crack propagation and fracture process zone(FPZ) by the reduction of rock fracture toughness under cyclic loading[J]. Engineering Geology，2016，208(1)：181–190.
[21]	戴峰，魏明东，徐奴文，等. 人字形切槽巴西圆盘Ⅰ型渐进断裂数值模拟研究[J]. 岩石力学与工程学报，2015，34(增2)：3 906–3 914. (DAI Feng，WEI Mingdong，XU Nuwen，et al. A numerical study of mode-I progressive rock fracture process of cracked cchevron notched Brazilian disc[J]. Chinese Journal of Rock Mechanics and Engineering，2015，34(Supp.2)：3 906–3 914.(in Chinese))