CO2碳化–矿渣/粉煤灰协同固化土效果与机制研究

doi:10.13722/j.cnki.jrme.2019.0940

Abstract
Figure/Table
References (0)
Related Citation (15)

Download: PDF (3787 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract Under the situation of increasingly serious global climate issue and increasingly urgent treatment of industrial solid wastes in China，how to effectively store CO2 and to use industrial wastes to prepare novel cementitious materials attracts significant attention from all around the worldwide. The combination of CO2 carbonation and industrial waste residues is an environmentally friendly and sustainable solidification technology，which cannot only sequester permanently CO2 emissions but make effective use of industrial residues and solidify soils. In order to explore the effect of many factors such as industrial residue content，carbonation mode and carbonation time on the carbonation effect，two kinds of bulk industrial wastes，i.e. slag and fly ash，were selected as binding materials to mix with soils and prepare samples for CO2 carbonation tests. The unconfined compressive strength(UCS) and pH detection tests were carried out to evaluate the mechanical properties of carbonated samples，and the X-ray diffraction(XRD)，mercury intrusion porosimetry(MIP) and scanning electron microscopy (SEM) tests were performed to reveal the microstructure evolution and carbonation mechanism. The test results show that the compressive strength of samples subjected to CO2 carbonation of 3 h raises by 5%～15%，and increases initially with waste residue content followed by a slight reduction or an almost constant. The carbonation effect varies greatly under different carbonation modes，and the optimal carbonation mode is proved to be confining pressure of 300 kPa and carbonation pressure of 150 kPa. The compressive strength of carbonated samples increases to the maximum at 3-6 h and then decreases as the carbonation time extends. The microscopic results reveal that CaCO3 crystals are formed and identified in the forms of aragonite and calcite within carbonated residue-solidified samples. These crystals can fill in the pore spaces and bond fine particles together，which without doubt contributes to the promotion of the compressive strength of carbonated samples. A reasonable prolongation in carbonation time produces more CaCO3 crystals and reduces the cumulative pore volume and quantity of large pores. However，the carbonate crystals are loosely arranged and fail to be firmly interconnected to form a reticulated skeleton skeletal structure，which leads to a limited improvement in the compressive strength of carbonated residue-solidified samples. This study can provide a preliminary basis for further research on the performance improvement of novel solidification technique combined industrial residue and CO2 carbonation.

Key words： soil mechanics')" href="#">

soil mechanics slag/fly ash CO2 carbonation compressive strength CO2 uptake amount ')" href="#">micro- mechanisms

	Service

	E-mail this article soil mechanics;slag/fly ash;CO2 carbonation;compressive strength;CO2 uptake amount;micro- mechanisms ”. Please open it by linking:https://rockmech.whrsm.ac.cn/EN/abstract/abstract31236.shtml" name="neirong">
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Dongxing1
	2
	3
	HE Fujin1
	2

Cite this article:

WANG Dongxing1,2,3, et al. Investigation on performance and mechanism of CO2 carbonated slag/fly ash solidified soils#br#[J]. , 2020, 39(7): 1493-1502.

URL:

https://rockmech.whrsm.ac.cn/EN/10.13722/j.cnki.jrme.2019.0940 OR https://rockmech.whrsm.ac.cn/EN/Y2020/V39/I7/1493

[1]	王萍，王炳才. 我国碳捕集与封存技术发展概况[J]. 天津商业大学学报，2016，36(4)：57-63.(WANG Ping，WANG Bingcai. Development situation of carbon capture and storage technology in China[J]. Journal of Tianjin University of Commerce，2016，36(4)：57-63.(in Chinese))
[2]	HUIJGEN W J J，RUIJG G J，COMANS R N J，et al. Energy consumption and net CO2 sequestration of aqueous mineral carbonation[J]. Industrial and engineering chemistry research，2006，45(26)：9 184-9 194.
[3]	常钧，吴昊泽. 钢渣碳化机制研究[J]. 硅酸盐学报，2010，38(7)：1 185-1 190.(CHANG Jun，WU Haoze. Study on carbonation mechanism of steel slag[J]. Journal of the Chinese Ceramic Society，2010，38(7)：1 185-1 190.(in Chinese))
[4]	吴昊泽，谭文杰，丁亮，等. 利用CO2气体碳酸化钢渣制备建材制品[J]. 混凝土与水泥制品，2010，(2)：28-30.(WU Haoze，TAN Wenjie，DING Liang，et al. Preparation of building materidls products with CO2 carbonation steel slag[J]. China Concreteand Cement Products，2010，(2)：24-27.(in Chinese))
[5]	蒋伟丽，卢豹，张峰，等. 矿渣碳化硬化过程的研究[J]. 硅酸盐通报，2017，36(2)：539-544.(JIANG Weili，LU Bao，ZHANG Feng，et al. Process of slag carbonization and hardening[J]. Bulletin of the Chinese Ceramic Society，2017，36(2)：539-544.(in Chinese))
[6]	郝园园，莫立武，恽进进. 碳化对镁渣砂浆强度和微观结构的影响[J]. 硅酸盐通报，2016，35(9)：3 047-3 052.(HAO Yuanyuan，MO Liwu，YUN Jinjin. Strength and microstructure of mortars prepared with magnesium slag after carbonation[J]. Bulletin of the Chinese Ceramic Society，2016，35(9)：3 047-3 052.(in Chinese))
[7]	张丰，莫立武，邓敏. 碳化养护对钢渣混凝土强度和体积稳定性的影响[J]. 硅酸盐学报，2016，44(5)：640-646.(ZHANG Feng，MO Liwu，DENG Min，et al. Effect of carbonation curing on mechanical strength and volume stability of steel slag concrete[J]. Journal of the Chinese Ceramic Society，2016，44(5)：640-646.(in Chinese))
[8]	MO L，PANESAR D K. Effects of accelerated carbonation on the microstructure of Portland cement pastes containing reactive MgO[J]. Cement and Concrete Research，2012，42(6)：769-777.
[9]	PANESAR D K，MO L. Properties of binary and ternary reactive MgO mortar blends subjected to CO2 curing[J]. Cement and Concrete Composites，2013，38：40-49.
[10]	张丰，莫立武，邓敏，等. 碳化对钢渣-水泥-CaO-MgO砂浆强度和微观结构的影响[J]. 建筑材料学报，2017，20(6)：854-861.(ZHANG Feng，MOLi-wu，DENG Min，et al. Effect of carbonation on mechanical and microstructure of mortars prepared with steel slag-cement-MgO-CaO blends[J]. Journal of Building Materials，2017，20(6)：854-861.(in Chinese))
[11]	曹菁菁. 活性氧化镁碳化固化土微观机理及应用研究[硕士学位论文] [D]. 南京：东南大学，2016.(CAO Jingjing. The application and micro- mechanism of carbonated reactive magnesia solidified soils[M. S. Thesis][D]. Nanjing：Southeast University，2016.(in Chinese))
[12]	郑旭，刘松玉，蔡光华，等. 活性MgO碳化固化土的干湿循环特性试验研究[J]. 岩土工程学报，2016，38(2)：297-304.(ZHENG Xu，LIU Songyu，CAI Guanghua，et al.Experimental study on drying- wetting properties of carbonated reactive MgO-stabilized soils[J]. Chinese Journal of Geotechnical Engineering，2016，38(2)：297-304.(in Chinese))
[13]	WANG D X，XIAO J，GAO X Y. Strength gain and microstructure of carbonated reactive MgO-fly ash solidified sludge from East Lake，China[J]. Engineering Geology，2019，251：37-47.
[14]	WANG D X，ZHU J Y，HE F J. CO2carbonation-induced improvement in strength and microstructure of reactive MgO- CaO-fly ash-solidified soils[J]. Construction and Building Materials，2019，229：116914.
[15]	张永. 碱激发胶凝材料的性能及微观研究[硕士学位论文][D]. 重庆：重庆大学，2017.(ZHANG Yong. Studyon the properties and microstructure of alkali activated cementitious materials[M. S. Thesis] [D]. Chongqing：Chongqing Jiaotong University，2017.(in Chinese))
[16]	张耀君，赵永林，李海宏，等. 水玻璃激发矿渣制备纳米地质聚合物研究[J]. 非金属矿，2009，32(1)：39-44.(ZHANG Yaojun，ZHAO Yonglin，LI Haihong，et al. Study on preparation of nano-geopolymer from slag powder activated by water glass[J]. Non- Metallic Mines，2009，32(1)：39-44.(in Chinese))