磷酸镁水泥固化铜污染土的冻融稳定性研究

doi:10.13722/j.cnki.jrme.2019.0720

Abstract
Figure/Table
References (0)
Related Citation (15)

Download: PDF (1928 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to study the strength characteristics and long-term stability of heavy metal contaminated soil，a series of strength and scanning electron microscope experiments were carried out based on solidified Cu-contaminated soil with magnesium phosphate cement. The freeze-thaw cycle times，magnesium phosphate cement content and copper ion concentration were considered as experiment effect factors，and the strength and microstructure of Cu-contaminated soil solidified were studied under freeze-thaw conditions. The results show that the unconfined compressive strength of solidified soil decreases gradually with the increase of freeze-thaw cycle times and copper ion concentration or the decrease of magnesium phosphate cement content. Under 3 and 12 freeze-thaw cycles，the reduction rate of unconfined compressive strength of solidified contaminated soil is the smallest，and the reduction rate of unconfined compressive strength reaches the peak value when the number of freeze-thaw cycles is 6 to 9 times. The freeze-thaw stability of Cu-contaminated soil of low concentration heavy metal that cured by magnesium phosphate cement is remarkable，and the freeze-thaw stability of solidified soil decreases with the increase of metal ion concentration. The micropore structure of solidified contaminated soil was obtained based on the scanning electron microscope experiment. The content of magnesium phosphate cement increased from 5% to 20%，and the percentage of microscopic statistical pores decreased by 17.43% when the concentration of copper ion was 0.5% and freeze-thawed for 6 times，so the mechanism of strength change is verified. The research provided theoretical and engineering application reference for frozen-thawed areas of northern China to evaluate the long-term stability of solidification treatment of heavy metal contaminated sites.

Key words： soil mechanics freeze-thaw cycle heavy metal contaminated soil solidification unconfined compressive strength microporosity

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HOU Shiwei 1
	ZHANG Hao1
	YANG Zhenji 1
	ZHANG Yuzhe 1
	ZHANG Yulong 1
	DING Zhaoyang 2

Cite this article:

HOU Shiwei 1,ZHANG Hao1,YANG Zhenji 1, et al. Study on freeze-thaw stability of Cu-contaminated soil solidified by magnesium phosphate cement[J]. , 2020, 39(S1): 3123-3129.

URL:

http://rockmech.whrsm.ac.cn/EN/10.13722/j.cnki.jrme.2019.0720 OR http://rockmech.whrsm.ac.cn/EN/Y2020/V39/IS1/3123

[1]	刘春阳，张宇峰，滕洁. 土壤中重金属污染的研究进展[J]. 污染防治技术，2006，14(3)：42–45.(LIU Chunyang，ZHANG Yongfeng，TENG Jie. Advances on Pollution Soils by Heavy Metals[J]. Pollution Control Technology，2006，14(3)：42–45.(in Chinese))
[4]	SINGH D，MANDALINKA V R，PARULEKAR S J. Magnesium potassium phosphate ceramic for 99Tcim mobilization[J]. Journal of Nuclear Materials，2006，348：272–282.
[8]	IYENGAR S R，TABBAA AI A. Developmental study of a low-pH magnusium phosphate cement for environmental applications[J]. Environmental Technology，2007，28：1 387–1 401.
[3]	JUENGER M C，WINNEFELD F，PROVIS J L. Advances in alternative cementitious binders[J]. Cement and Concrete Research，2011，41(12)：1 232–1 243.
[6]	刘晶晶，查甫生，郝爱玲，等. NaCl侵蚀环境下水泥固化铬污染土的强度及淋滤特性[J]. 岩土力学，2015，36(10)：2 855–2 861.(LIU Jingjing，CHA Pusheng，HAO Ailing，et al. Strength and leaching characteristics of chromium polluted soil solidified with cement in a NaCl erosion environment[J]. Rock and Soil Mechanics，2015，36(10)：2 855–2 861.(in Chinese))
[13]	张泽，马巍，齐吉琳. 冻融循环作用下土体结构演化规律及其工程性质改变机理[J]. 吉林大学学报：地球科学版，2013，43(6)：1 904–1 914.(ZHANG Ze，MA Wei，QI Jilin. Structure evolution and mechanism of engineering properties change of soils under effect of freeze-thaw cycle[J]. Journal of Jilin University：Earth Science，2013，43(6)：1 904–1 914.(in Chinese))
[2]	章定文，项莲，曹智国. CaO对钙矾石固化/稳定化重金属铅污染土的影响[J]. 岩土力学，2018，39(1)：29–35.(ZHANG Dingwen，XIANG Lian，CAO Zhiguo. Effect of CaO on ettringite stabilization/ solidification of lead-contaminated soil[J]. Rock and Soil Mechanics，2018，39(1)：29–35.(in Chinese))
[5]	BUJ I，TORRAS J，CASELLAS D，et al. Leaching behaviour of magnesium phosphate cements containing high quantities of heavy metals[J]. Journal of Hazardous Materials，2010，175(12)：789–794.
[7]	陈蕾，刘松玉，杜延军. 水泥固化重金属铅污染土的强度特性研究[J]. 岩土工程学报，2010，32(12)：1 898–1 903.(CHEN Lei，LIU Songyu，DU Yanjun. Unconfined compressive strength properties of cement solidified/stabilized lead-contaminated soils[J]. Chinese Journal of Geotechnical Engineering，2010，32(12)：1 898–1 903.(in Chinese))
[10]	魏明俐，伍浩良，杜延军，等. 冻融循环下含磷材料固化锌铅污染土的强度及溶出特性研究[J]. 岩土力学，2015，36(增1)：215–219.(WEI Mingli，WU Haoliang，DU Yanjun，et al. Experimental study of Zn and Pb contaminated soils stabilized with new phosphate-based binder under freeze-thaw cycles[J]. Rock and Soil Mechanics，2015，36(Supp.1)：215–219.(in Chinese))
[12]	查甫生，刘晶晶，郝爱玲，等. Nacl侵蚀环境下水泥固化铅污染土强度及微观特性试验研究[J]. 岩石力学与工程学报，2015， 34(增2)：4 325–4 332(CHA Fusheng，LIU Jingjing，HAO Ailing，et al. Experimental study of strength and microstructure characteristics of cement solidified lead contaminated soil eroded by sodium chkoride solution[J]. Chinese Journal of Rock Mechanics and Engineering，2015，34(Supp.2)：4 325–4 332.(in Chinese))
[14]	邵俐，刘佳，丁勇，等. 水泥固化镍污染土的强度和微观结构特性研究[J]. 水资源与水工程学报，2014，25(2)：75–80.(SHAO Li，LIU Jia，DING Yong，et al. Research on strength and microstructure characteristics of cement solidified nickel contaminated soil[J]. Journal of Water Resources and Water Engineering，2014，25(2)：75–80.(in Chinese))
[11]	王连斌. 碱渣固化重金属污染土的工程性质试验研究[硕士学位论文][D]. 合肥：合肥工业大学，2016.(Wang Lianbin. Research on engineering properties of soda residue solidified/stabilized heavy mental contaminated soils[M. S. Thesis][D]. Hefei：Hefei University of Technology，2016.(in Chinese))
[9]	刘士雨，俞缙，韩亮，等. 三合土表面微生物诱导碳酸钙沉淀耐水性试验研究[J]. 岩石力学与工程学报，2019，38(8)：1 718– 1 729.(LIU Shiyu，YU Jin，HAN Liang，et al. Experomental study on water resistance of tabia surface with microbially induced carbonate precipitation[J]. Chinese Journal of Rock Mechanics and Engineering，2019，38(8)：1 718–1 729.(in Chinese))